| Product code | Packing specification | Colour | Compressive strength | Shear strength | hardness | Operating temperature | Mixing ratio(A:B) | Operating time | Curing rate25℃ | peculiarity | ||
| Weight ratio | Volume ratio | 50%load | Full mechanical load | |||||||||
| TS801 | 1.1kg | 淺棕 | / | 77N/25mm(剝離強度） | / | -50~110 | 10:01 | / | 40 | 2 | 8 | ◎ Polyurethane two-component fast curing, high strength, bonding without heating, pressure ◎ It is mainly used for cold bonding of multi-layer core rubber conveyor belt joints, and can also be used for bonding between rubber - rubber, rubber - metal, like glue - fabric ◎ The initial viscosity is strong, and the load can be run 30 minutes after sticking |
| TS802 | 350g | 黑色 | 斷裂伸長率200% | 拉伸強度3.5Mpa | 73（shoreA） | -50~100 | 2:01 | / | 10 | 12 | 24 | ◎ Medium strength, medium hardness ◎ Used to repair transport belt, cable, roller and other local damage, cable joint insulation seal, can also be used as equipment anti-cavitation lining coating and mechanical seal plugging |
| TS8101 | 500g | 灰色 | 98 | 20 | 82 | -60~150 | 2:01 | 1.7:1 | 45 | 12 | 24 | ◎ Universal, two-component, thixotropic, good operability ◎ It is used to repair pores, shrinkage holes, sand holes, cracks, and to fill dimensional aberrations and scratches ◎ Impact resistance, corrosion resistance, paint film adhesion |
| TS811 | 250g/500g | 鑄鐵色 | 110 | 20 | 85 | -60~160 | 7:01 | 4:01 | 45 | 12 | 24 | ◎ Suitable for the repair of pores, holes and cracks in iron castings ◎ Wear resistance and corrosion resistance, close to the color of the matrix after repair ◎ Can be used to fill the size of the repair and wear, after curing with the body of high bonding strength |
| TS812 | 250g/500g | 鋼色 | 106 | 20 | 85 | -60~160 | 7:01 | 4:01 | 45 | 12 | 24 | ◎ Suitable for all kinds of carbon steel, alloy steel defect repair and parts wear, scratch, corrosion, fracture repair ◎ Wear resistance and corrosion resistance, close to the color of the matrix after repair ◎ High bonding strength with the body after curing |
| TS813 | 250g/500g | 鋁色 | 99 | 19 | 82 | -60~160 | 6:01 | 4:01 | 45 | 12 | 24 | ◎ It is suitable for repairing defects such as pores, sand holes, shrinkage holes and scratches, cracks and wear of cast aluminum parts ◎ Wear resistance, corrosion resistance, good heat resistance ◎ After repair, the color is close to the matrix. High strength after curing |
| TS851 | 114g | 鋼色 | / | 20 | 75 | -50~150 | / | / | 4 | 20(min) | 6 | ◎ Used for bonding and plugging, repairing defects, installation, fixing, sample production and many other purposes ◎ Special mastic form, can be directly used by hand, do not drip, do not flow Fast curing, timely repair, easy to use |
| TS856 | 500g | 棕色 | / | 20 | 82 | -50~150 | 6:01 | 3.5:1 | 10 | 12 | 24 | ◎ It is mainly used for plugging and sealing of various pipelines, valves, radiators, boats, oil tanks and water tanks. ◎ For emergency repair in humid environment. |
| TS858 | 85g | 琥珀色 | / | 19 | 85 | -50~150 | 1:01 | 1:01 | 3 | 12 | 24 | ◎ Liquid, quick positioning, with oil repair. ◎ Used for the repair of oil leakage and leakage of transformer, oil tank, oil tank, tubing, flange and other equipment. (Note: not suitable for copper pipeline plugging) |